| . [[ http://metglas.com/products/magnetic_materials/2605SA1.asp | Metglas 2605SA1 ]] looks good, higher temperature than 2605HB1M. . [[ attachment:2605sa1.pdf | datasheet ]] downloaded 2017/02/11 |
[[ http://metglas.com/products/magnetic_materials/2605SA1.asp | Metglas 2605SA1 ]] looks good, higher temperature than 2605HB1M. [[ attachment:2605sa1.pdf | datasheet ]] downloaded 2017/02/11 |
Rotor Lamination
Laminated launch loop rotors will have good magnetic properties and will rapidly disperse and oxidize in the atmosphere after a rotor-release catastrophe.
Metglas 2605SA1 looks good, higher temperature than 2605HB1M. datasheet downloaded 2017/02/11
Metglas 2605SA1 |
||||
Curie temperature |
395C / 668K |
|
saturation induction |
1.56 Tesla |
thickness |
23 μm |
|
density |
7.18 g/cm³ |
Thermal Expansion |
7.6 ppm/°C |
|
|
|
Tensile Strength |
1 GPa |
|
Elastic Modulus |
100 GPa |
Iron |
85 to 95% |
|
2.5g/m³ |
|
Silicon |
5 to 10% |
|
3.0g/m³ |
|
Boron |
1 to 5% |
|
2,0g/m³ |
|
resistivity |
1.3 μΩ-m |
|
|
|
60 Hz and 1.4 T |
|
Induction at 80 A/m |
≥1.35 T |
|
Core Loss |
≤0.17 W/kg |
|
Exciting Apparent Power* |
1.1 (VA/kg) |
The core loss appears proportional to (frequency × flux )² .