| || Material || density || elastic || strength || CTE || Vsound || Support || 100km || Therm exp || || || || modulus || || || || Length || Round Trip || 100Km*100K || || || gm/cm^3^ || GPa || MPa || um/m-K || km/s || km || seconds || m || || || || || || || || || || || || Steel SAE980x || 7.9 || 200 || 650 || 12 || 5.0 || 8.4 || 40 || 120 || || Pure Kevlar || 1.44 || 124 || 3620 || -2.7 || 9.3 || 250 || 22 || -27 || || Pure Spectra || 0.97 || 168 || 2580 || || 13.2 || 270 || 15 || || || Pure Diamond || 3.52 || 1140 || >60000 || 1.2 || 18.0 || 1740 || 11 || 12 || || Pure nanotube || || || || || || || || || || composites: || || || || || || || || || || 80% Kevlar || || || || || || || || || || 80% Spectra || || || || || || || || || || 80% nanotube || || || || || || || || || |
|| Material || density || elastic || strength || CTE || Vsound || Support || 100km || Therm exp || notes || || || || modulus || || || || Length || Round Trip || 100Km*100K || || || || gm/cm^3^ || GPa || GPa || um/m-K || km/s || km || seconds || m || || || || || || || || || || || || || || Steel SAE980x || 7.9 || 200 || 0.65 || 12 || 5.0 || 8.4 || 40 || 120 || || || Pure Kevlar || 1.44 || 124 || 3.62 || -2.7 || 9.3 || 250 || 22 || -27 || || || Pure Spectra || 0.97 || 168 || 2.58 || -12 || 13.2 || 270 || 15 || -120 || continuous creep || || Pure Diamond || 3.52 || 1140 || >60 || 1.2 || 18.0 || 1700 || 11 || 12 || || || Pure nanotube || ~1.4 || ~1000 || ~60 || -9? || 26.0 || 4400 || 8 || -90 || || || composites: || || || || || || || || || || || 80% Kevlar || || || || || || || || || || || 80% Spectra || || || || || || || || || || || 80% nanotube || || || || || || || || || || note: Nanotube properties are controversial. The CTE simulation [[ etd.lib.fsu.edu/theses/available/etd-08262005-003434/.../Thesis.pdf | Prakash ]] is used here, but other simulations differ wildly. |
Linear Cables
Stabilization and elevator cables on the launch loop are very long, and propagation delay is a big issue. In most systems people are familiar with, cables are short enough and forces change slowly enough that propagation delay is not a major issue. With a launch loop, forces can change rapidly (milliseconds) while the propagation delays are 10s of seconds.
For example, when an instantaneous force change is applied to one end of a very long cable, the end does not stretch a little, it moves, and keeps moving until the force has had time to propagate to a stationary attachment and back. For a 100km stabilization cable, and a 10km/s speed of sound, that can be 20 seconds, in which time many meters of cable moves.
Material |
density |
elastic |
strength |
CTE |
Vsound |
Support |
100km |
Therm exp |
notes |
|
|
modulus |
|
|
|
Length |
Round Trip |
100Km*100K |
|
|
gm/cm3 |
GPa |
GPa |
um/m-K |
km/s |
km |
seconds |
m |
|
|
|
|
|
|
|
|
|
|
|
Steel SAE980x |
7.9 |
200 |
0.65 |
12 |
5.0 |
8.4 |
40 |
120 |
|
Pure Kevlar |
1.44 |
124 |
3.62 |
-2.7 |
9.3 |
250 |
22 |
-27 |
|
Pure Spectra |
0.97 |
168 |
2.58 |
-12 |
13.2 |
270 |
15 |
-120 |
continuous creep |
Pure Diamond |
3.52 |
1140 |
>60 |
1.2 |
18.0 |
1700 |
11 |
12 |
|
Pure nanotube |
~1.4 |
~1000 |
~60 |
-9? |
26.0 |
4400 |
8 |
-90 |
|
composites: |
|
|
|
|
|
|
|
|
|
80% Kevlar |
|
|
|
|
|
|
|
|
|
80% Spectra |
|
|
|
|
|
|
|
|
|
80% nanotube |
|
|
|
|
|
|
|
|
|
note: Nanotube properties are controversial. The CTE simulation Prakash is used here, but other simulations differ wildly.